The goal of the research is preparation of SiAlON-containing composite through nitro aluminothermic processes, by the methods of reactive sintering and hot compaction.

Method: The composite CH-6 was obtained by the method of reactive sintering, with further grinding in attritor and hot compression in vacuum furnace at 1620°C, under 30 MPa pressure and 10-12 min standing at the final temperature. Precursor was prepared in a thermostat at 150°C temperature by double compression. Pressure equaled to 20-25 MPa.  Results: Physical-technical properties of specimens prepared via hot compaction were investigated. Mechanical strength at compression is 1940 MPa; mechanical strength at bending is 490 MPa; elastic module is 199.5 GPa, HV-11.6 GPa. X-Ray diffraction analysis, optical, electron microscopic and X-ray diffraction Microspectral analysis were used to investigate composite microstructure and phase composition, with raster electron microscope “Nanolab 7” of the company "OPTON”. The values of the electrical parameters of the study composites were calculated on the basis of the obtained "lg p- t" dependence.  Composite formulation was defined, the main phases of which were: β-SiAlON, corundum nano particles (‘ALCOA” Germany) and silicium carbide.                                                                                              Conclusion: Composite CH-6 has been selected from the obtained composites, which is characterized by relatively high physical-technical properties: strength, density and hardness. Materials can be used for making high refractory articles, such as jackets to secure thermocouples, furnace bedding, cutting tools for metal and wood treatment, in rocket spatial technology and others.

Key words: composite, electron, microscope, phase composition, β-SIAlON.  

Resume: Objective - to obtain SIALON containing composites by reactive sintering method in SiC-B4C-Si-Al-Al2O3 –Carbon fiber system. Using this method of synthesis, it became possible to obtain composites with different percentages of SIALON. Our task was also to study the phase composition in the SiC-B4C-Si-Al-Al2O3 system.

Method. To study the phase composition of the compo-sites, we conducted an X-ray structural analysis on the DRON-3 device, and to study the microstructure, we conducted research on an optical microscope and a ras-ter electron microscope “Nanolab 7” of the company "OPTON”.

Result. In SiC-B4C-Si-Al-Al2O3-Carbon fiber system we obtained composites with a matrix composed of: β-SIALON, silicon carbide, corundum and nano particles of boron nitride.

Conclusion. The phase composition of the obtained composite provides high physical-technical and per-formance properties of these composites. Key words: composite; electron microscope; phase composition; β-SIALON.

ტექნიკის სწრაფი განვითარების პირობებში, სულ უფრო აქტუალური ხდება ისეთი მასალების მიღების აუცილებლობა , რომლებიც იმუშავებენ მაღალი ტემპერატურის პირობებში საექსპლუატაციო თვისებების შენარჩუნებით. ამ თვალსაზრისით პერსპექტიულია ძნელადლღობადი კარბიდების, ბორიდებისა და ნიტრიდების ბაზაზე მიღებული კერამიკული მასალების გამოყენება.

დისერტაციის რეცენზირება

სამაგისტრო ნაშრომების ხელმძღვანელობა

სადოქტორო თემის ხელმძღვანელობა/თანახელმძღვანელობა

უცხოურ ენებზე მონოგრაფიის სამეცნიერო რედაქტირება

ქართულ ენაზე მონოგრაფიის სამეცნიერო რედაქტირება

რეფერირებული ან პროფესიული ჟურნალის/ კრებულის მთავარი რედაქტორობა

სამეცნიერო პროფესიული ჟურნალის/ კრებულის რეცენზენტობა

რეფერირებული სამეცნიერო ან პროფესიული ჟურნალის/ კრებულის სარედაქციო კოლეგიის წევრობა

საერთაშორისო ორგანიზაციის მიერ მხარდაჭერილ პროექტში/გრანტში მონაწილეობა

სახელმწიფო ბიუჯეტის სახსრებით მხარდაჭერილ პროექტში/ გრანტში მონაწილეობა

პატენტის ავტორობა

უფლება ქართულ ან უცხოურ სასაქონლო ნიშანზე, სასარგებლო მოდელზე

საქართველოს მეცნიერებათა ეროვნული აკადემიის ან სოფლის მეურნეობის აკადემიის წევრობა

საერთაშორისო პროფესიული ორგანიზაციის წევრობა

კონფერენციის საორგანიზაციო/ საპროგრამო კომიტეტის წევრობა

ჯილდო ეროვნული/ დარგობრივი პრემია, ორდენი, მედალი და სხვ.

საპატიო წოდება

მონოგრაფია

სახელმძღვანელო

სტატია მაღალ რეიტინგულ და ადგილობრივ ჟურნალებში

პუბლიკაცია სამეცნიერო კონფერენციის მასალებში, რომლებიც ინდექსირებულია Web of Science-ში და Scopus-ში